Liquid Polysulfide Polymer
- Company Name:Royenterprise
- Membership:Free Member
- Member Since:2014. 09.24
- Country/Region:Greenland
- City:Athens
- Contact:roy
- Related Keywords:liquid polysulfide polymer
Specifications
1.Excellent resistance to low and high temperature
2.Very low water absorption
liquid polysulfide polymer
1.Excellent resistance to low and high temperature
2.Very low water absorption
YULONG liquid polysulfide polymer
YL P2-2
Polysulfides are one of the older polymer technologies for the manufacture of high-performance sealants. Despite a decline in popularity, they continue to be used in many parts of the world.
Product Use:
1: Glue-coating before glue coping withered material surface cleaning, clean before coating. Otherwise, it will affect the adhesive seal.
2: Takes out A and B two components according to 10: 1 proportion to carry on the mix agitation to be even, achieves the achromatism.
3: Manual or mechanical operation must arrange a direction coating and put some pressure, prevent the air wrapped into.
4: Construction of the ambient temperature maintained at above 5 ° C
Storage:
Store all materials in unopened containers in a dry area.Protect from heat and direct sunshine
Colour:
Part A (Base): White
Part B (Curing Agent): Black and Grey
After Mixed: Black and Grey
Packing details:
1. Machine : A group were 300kg, B group were 30kg (barrels package)
2. Manual: (1). A group were 30kg, B component 3kg (barrels package) or Per buyer’s demand
TECHNICAL DATA SHEET
|
Item |
Detail |
Result |
|
Aspect/Appearance |
Base/Part A |
White Paste |
|
Curing Agent/Part B |
Black Paste |
|
|
Viscosity, Pa·s |
Base/Part A |
4,000 |
|
Curing Agent/Part B |
800 |
|
|
Specific Gravity |
Base/Part A |
1.6 |
|
Curing Agent/Part B |
1.5 |
|
|
Mixed Component A and Component B at 10:1 by weight,under the conditions of 23±2oC and the R.H. of 50±5%,after 7days of curing |
||
|
Application Temperature,°C |
Value |
5~45 |
|
Aspect/Appearance |
As mixed |
Black, Non-slump Paste |
|
Working time ,min |
Value |
20~60 |
|
Tacking-Free time, min |
Value |
20~60 |
|
Service Temperature,°C |
Value |
-50 ~+100 |
|
Hardness, Shore A |
|
38 |
|
Peel Strength ,MPa |
Value |
2.05 |
|
Tensile strength, MPa |
|
0.8 |
|
Elongation ,% |
At Break |
174 |